Process for producing a thiometallate or a selenometallate material

ABSTRACT

A method for producing a thiometallate or selenometallate material is provided in which a first salt containing an anionic component selected from the group consisting of MoS 4   2− , MoSe 4   2− , WS 4   2− , WSe 4   2− , VS 4   3− , and VSe 4   3− , and a second salt containing a cationic component comprising a metal in any non-zero oxidation state selected from the group consisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, Pb, Cd, Sb, Ge, Ga, In, Au, Hg are mixed under anaerobic conditions in an aqueous mixture at a temperature of from 15° C. to 150° C.

CROSS REFERENCE TO RELATED APPLICATION

The present application claims the benefit of priority from U.S.Provisional Patent Application Ser. No. 61/297,084 filed Jan. 21, 2010.

FIELD OF THE INVENTION

The present invention is directed to a process for producing athiometallate or selenometallate material. In particular, the presentinvention is directed to a process for producing a bimetallic orpolymetallic thiometallate or selenometallate material.

BACKGROUND OF THE INVENTION

Increasingly, resources such as heavy crude oils, tar sands, shale oils,and coal are being utilized as hydrocarbon sources due to decreasingavailability of easily accessed light sweet crude oil reservoirs. Theseresources are disadvantaged relative to light sweet crude oils, oftencontaining significant amounts of sulfur, nitrogen, metals, and heavyhydrocarbon fractions including residue and asphaltenes. Thedisadvantaged crudes typically require a considerable amount ofupgrading in order to obtain useful hydrocarbon products therefrom.

Numerous catalysts have been developed for catalytically hydrocrackingand hydrotreating disadvantaged hydrocarbon feedstocks. Typically, thesecatalysts contain a Group VIB or Group VIII metal supported on a carrierformed of alumina, silica, or alumina-silica. Such catalysts arecommonly sulfided to activate the catalyst, either before contacting thecatalyst with a disadvantaged hydrocarbon feed or in situ with thedisadvantaged hydrocarbon feed.

Applicants have discovered that a bimetallic or polymetallicthiometallate or selenometallate material is an exceptionally goodcatalyst for upgrading disadvantaged hydrocarbon feedstocks,particularly for converting all or substantially all heavy fractionssuch as residue and asphaltenes in the feedstock to lighter fractionswhile forming little or no coke. In particular, Applicants havediscovered that bimetallic tetrathiomolybdates, tetrathiotungstates, andtetrathiovanadates and/or polymetallic tetrathiomolybdates,tetrathiotungstates, and tetrathiovanadates, and theirtetraseleno-analogs are especially effective for hydrocrackingdisadvantaged hydrocarbon feedstocks to upgrade the feedstocks.

Ammonium and alkylammonium thiometallates have been used as precursorsto produce metal sulfides. For example, tetralkylammonium thiomolybdate,tetralkylammonium thiotungstate, and ammonium thiomolybdate precursorcompounds have been treated at temperatures of above 350° C. tothermally decompose the precursor compounds to produce MoS₂ and WS₂disulfides having predicable stoichoimetry that have a high surface areaand show substantial hydrodesulfurization and hydrodenitrogenationcatalytic activity. Ammonium thiometallates have also been used asprecursors to produce bimetallic compounds in an organic solvent. Forexample, copper thiometallates and copper selenometallates have beenproduced using a solvothermal method by reacting (NH₄)₂MoS₄, (NH₄)₂WS₄,(PPh₄)₂MoSe₄, or (PPh₄)₂WSe₄ with copper borofluoride salts in organicsolvents at temperatures of 110° C. or above in an autoclave atautogenous pressures. Iron-molybdenum sulfide compounds have beenproduced by dissolving (NH₄)₂MoS₄ in an organic chelating solution ofdiethylenetriamine (dien) and slowly adding an iron salt in a 10%aqueous dien solution to precipitate a hydrodenitrogenation catalystprecursor. The precursor is thermally decomposed to remove organicligand constituents and sulfactivate the catalyst. Such methods may beimpractical for producing high yields of bimetallic or polymetallicthiometallates having a high surface area in a cost effective manner dueto the temperatures, pressures, and solvents required, or due to thenature of the products themselves.

A method of preparing copper tetrathiomolybdates from ammoniumtetrathiomolybdates and a copper salt is described in TheCopper-Molybdenum Antagonism in Ruminants. III. Reaction of Copper(II)with Tetrathiomolybdate(VI), Laurie, Pratt, & Raynor, Inorganica ChimicaActa, 123 (1986) 193-196. Aqueous solutions of reactants CuSO₄.5H₂O andM₂ ^(I)-MoS₄ (M^(I)=NH₄ ⁺, Et₄N⁺, or Na⁺) and (NH₄)₂MoS₄ were mixed toform a solid product which was collected by filtration, washed, and thendried. The solid product contained two materials, a compositionM^(I)CuMoS₄ (where M^(I) is the M^(I) included in the tetrathiomolybdatereactant) and a composition CuMoS_(4-x)O_(x), where x=2 or 3.

Improved processes are desirable for producing non-copper thiometallateor selenometallate materials, particularly bimetallic or polymetallicthiometallate or selenometallate materials.

SUMMARY OF THE INVENTION

The present invention is directed to a method for producing athiometallate or selenometallate material, comprising:

mixing a first salt and a second salt in an aqueous mixture underanaerobic conditions, where, during mixing the aqueous mixture has atemperature of from 15° C. to 150° C., and wherein the first saltcomprises a cationic component containing one or more metals selectedfrom the group consisting of an alkali metal, an alkaline earth metal,and mixtures thereof and comprises an anionic component containing afirst metal selected from the group consisting of Mo, W, and V where theanionic component is selected from the group consisting of MoS₄ ²⁻,MoSe₄ ²⁻, WS₄ ²⁻, WSe₄ ²⁻, VS₄ ³⁻, and VSe₄ ³⁻ and mixtures thereof, andwherein the second salt comprises a cationic component comprising asecond metal in any non-zero oxidation state selected from the groupconsisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr,Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn and mixtures thereof, where the firstand second salts are soluble in the aqueous mixture;

separating a solid material from the aqueous mixture comprising a) thefirst metal; and b) the second metal, wherein at least a portion of thesolid material separated from the aqueous mixture has a structureaccording to a formula selected from the group consisting of formula(I), formula (II), formula (III), and formula (IV):

where M is either the first metal or the second metal; at least one M isthe first metal and at least one M is the second metal; and Q is eithersulfur or selenium;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed to a method for producing athiometallate or a selenometallate material, in particular, atetrathiometallate or a tetraselenometallate material. The method isconducted in an aqueous solution at low temperatures compared to thermalsolvolysis methods, which typically are effected at temperatures above150° C. As such, bulk quantities of the thiometallate or selenometallatematerials may be easily produced at relatively low cost. The methodproduces a polymeric tetrathiometallate or tetraselenometallate materialthat is substantially free of oxygen contaminants and contaminantsderived from tetrathio- or tetraselenometallate salt counterions such asammonium, sodium, or potassium. The method is also effective to producesignificant quantities of the polymeric tetrathiometallate ortetraselenometallate material as small or nano particles having a largesurface area that are effective as a catalyst for hydrocracking a heavyhydrocarbon feedstock.

As used herein, the phrase “anaerobic conditions” means “conditions inwhich less than 0.5 vol. % oxygen gas is present”. For example, aprocess that occurs under anaerobic conditions, as used herein, is aprocess that occurs in the presence of less than 0.5 vol. % oxygen gas.Anaerobic conditions may be such that no detectable oxygen gas ispresent.

“ASTM” as used herein refers to American Standard Testing Method.

The term “aqueous” as used herein is defined as containing more than 50vol. % water. For example, an aqueous solution or aqueous mixture, asused herein, contains more than 50 vol. % water.

The term “dispersible” as used herein with respect to mixing a solid,such as a salt, in a liquid is defined to mean that the components thatform the solid, upon being mixed with the liquid, are retained in theliquid for a period of at least 24 hours upon cessation of mixing thesolid with the liquid. A solid material is dispersible in a liquid ifthe solid or its components are soluble in the liquid. A solid materialis also dispersible in a liquid if the solid or its components form acolloidal dispersion or a suspension in the liquid.

The term “ligand” as used herein is defined as a molecule or ionattached to, or capable of attaching to, a metal ion in a coordinationcomplex.

The term “monomer” as used herein is defined as a molecular compoundthat may be reactively joined with itself or another monomer in repeatedlinked units to form a polymer.

The term “polymer” as used herein is defined herein as a compoundcomprised of repeated linked monomer units.

As used herein, an element of the Periodic Table of Elements may bereferred to by its symbol in the Periodic Table. For example, Cu may beused to refer to copper, Au may be used to refer to gold, Hg may be usedto refer to mercury etc.

The term “soluble” as used herein refers to a substance a majority (e.g.greater than 50 wt. %) of which dissolves in a liquid upon being mixedwith the liquid at a specified temperature and pressure. For example, amaterial dispersed in a liquid is soluble in the liquid if less than 50wt. % of the material may be recovered from the liquid by centrifugationand filtration.

In the process of the present invention, a first salt comprised of ananionic component containing a first metal selected from the groupconsisting of Mo, W, and V and a second salt comprised of a cationiccomponent containing a metal are mixed in an aqueous mixture underanaerobic conditions at a temperature of from 15° C. to 150° C., and asolid material is separated from the aqueous mixture where the separatedsolid material contains a) the first metal of the anionic component ofthe first salt; and b) the second metal of the cationic component of thesecond salt, wherein at least a portion of the solid material separatedfrom the aqueous mixture has a structure according to a formula selectedfrom the group consisting of formula (I), formula (II), formula (III),and formula (IV);

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, and Q iseither sulfur or selenium;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃.

The first salt utilized in the process of the present invention includesan anionic component that is a tetrathiometallate or atetraselenometallate, where the metal of the anionic component of thefirst salt is selected from the group consisting of molybdenum,tungsten, and vanadium and is defined herein as the first metal. Inparticular, the first salt contains an anionic component that isselected from the group consisting of MoS₄ ²⁻, MoSe₄ ²⁻, WS₄ ²⁻, WSe₄²⁻, VS₄ ³⁻, and VSe₄ ³⁻.

The first salt also contains a cationic component associated with theanionic component of the first salt to form the first salt. The cationiccomponent of the first salt may be selected from alkali metal andalkaline earth metal counterions to the tetrathiometallate or thetetraselenometallate anionic component of the first salt so long as thecombined cationic component and the anionic component of the first saltform a salt that is dispersable, and preferably soluble, in the aqueousmixture in which the first salt and the second salt are mixed, and solong as the cationic component of the first salt does not prevent thecombination of the anionic component of the first salt with the cationiccomponent of the second salt in the aqueous mixture to form the solidproduct material. Preferably, the cationic component balances the chargeof the anionic component in the first salt. In a preferred embodiment,the cationic component of the first salt comprises one or more sodiumions, or one or more potassium ions.

Certain compounds are preferred for use as the first salt in the processof the present invention. In particular, the first salt is preferablyselected from the group consisting of Na₂MoS₄, Na₂WS₄, Na₃VS₄, K₂MoS₄,K₂WS₄, K₃VS₄, Na₂MoSe₄, Na₂WSe₄, K₂MoSe₄, K₂WSe₄, K₃VSe₄, K₃WSe₄ andhydrates thereof.

The first salt may be produced from a commercially availabletetrathiomolybdate, tetrathiotungstate, or tetrathiovanadate salt. Forexample, the first salt may be produced from ammoniumtetrathiomolybdate, ammonium tetrathiotungstate, or from ammoniumtetrathiovanadate. The first salt may be formed from the commerciallyavailable ammonium tetrathiometallate salts by exchanging the cationicammonium component of the commercially available salt with a desiredalkali or alkaline earth cationic component from a separate salt. Theexchange of the cationic components to form the desired first salt maybe effected by mixing the commercially available salt and the saltcontaining the desired cationic component in an aqueous solution to formthe desired first salt.

A method of forming the first salt is to disperse an ammoniumtetrathiomolybdate, ammonium tetrathiotungstate, or ammoniumtetrathiovanadate salt in an aqueous solution, preferably water, and todisperse an alkali metal or alkaline earth metal cationic componentdonor salt, preferably a carbonate, in the aqueous solution, where thecationic component donor salt is provided in an amount relative to theammonium tetrathiomolybdate, ammonium tetrathiotungstate, or ammoniumtetrathiovanadate salt to provide a stoichiometrially equivalent orgreater amount of its cation to ammonium of the ammoniumtetrathiomolybdate, ammonium tetrathiotungstate, or ammoniumtetrathiovanadate salt. The aqueous solution may be heated to atemperature of at least 50° C., or at least 65° C. up to 100° C. toevolve ammonia from the ammonium containing salt and carbon dioxide fromthe carbonate containing salt as gases, and to form the second salt. Forexample a Na₂MoS₄ salt may be prepared for use as the first salt bymixing commercially available (NH₄)₂MoS₄ and Na₂CO₃ in water at atemperature of 70° C.-80° C. for a time period sufficient to permitevolution of a significant amount, preferably substantially all, ofammonia and carbon dioxide gases from the solution, typically from 30minutes to 4 hours, and usually about 2 hours.

The first salt may be contained in an aqueous solution or an aqueousmixture, where, in the process of the present invention, the aqueoussolution or aqueous mixture containing the first salt (hereinafter the“first aqueous solution”) may be mixed with the second salt or anaqueous solution containing the second salt (hereinafter the “secondaqueous solution”) in the aqueous mixture to form the solid productmaterial. The first salt is preferably dispersible, and most preferablysoluble, in the first aqueous solution and is dispersible, andpreferably soluble, in the aqueous mixture of the first and secondsalts. The first aqueous solution contains more than 50 vol. % water, orat least 75 vol. % water, or at least 90 vol. % water, or at least 95vol. % water, and may contain more than 0 vol. % but less than 50 vol.%, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of anorganic solvent containing from 1 to 5 carbons selected from the groupconsisting of an alcohol, a diol, an aldehyde, a ketone, an amine, anamide, a furan, an ether, acetonitrile, and mixtures thereof. Theorganic solvent present in the first aqueous solution, if any, should beselected so that the organic compounds in the organic solvent do notinhibit reaction of the anionic component of the first salt with thecationic component of the second salt upon forming an aqueous mixturecontaining the first aqueous solution, e.g., by forming ligands or byreacting with the first or second salts or their respective cationic oranionic components. Preferably, the first aqueous solution contains noorganic solvent. Most preferably the first aqueous solution consistsessentially of water, most preferably deionized water, and the firstsalt, although in a less preferred embodiment the first aqueous solutionmay contain compounds other than the first salt, such as a buffercompound.

If the first salt is contained in a first aqueous solution, theconcentration of the first salt in the first aqueous solution may beselected to promote formation of a solid product material having aparticle size distribution with a small mean and/or median particle sizeand having a relatively large surface area per particle upon mixing thefirst salt and the second salt in the aqueous mixture. It has been foundthat decreasing the instantaneous concentration of the first salt and/orthe second salt during mixing in the aqueous mixture produces a solidproduct material comprised of smaller particles relative to solidproduct materials produced from an aqueous mixture containing higherinstantaneous concentrations of the first and second salts, where thesmall particles have a relatively large surface area. In an embodimentof the process of the invention, the first aqueous solution may containat most 0.8 moles per liter, or at most 0.6 moles per liter, or at most0.4 moles per liter, or at most 0.2 moles per liter, or at most 0.1moles per liter of the first salt.

The second salt utilized in the process of the present inventionincludes a cationic component comprising a metal in any non-zerooxidation state selected from the group consisting of Fe, Ag, Co, Mn,Re, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi,Sn, Pb, Cd, Sb, Ge, Ga, In, Au, Hg, and mixtures thereof, defined hereinas the second metal. The cationic component of the second salt containsat most 1 part per million of copper, and preferably contains no copper.The cationic component of the second salt may consist essentially of ametal selected from the group consisting of Fe, Ag, Co, Mn, Re, Rh, Pd,Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, Pb, Cd,Sb, Ge, Ga, In, Au, Hg, and mixtures thereof. The cationic component ofthe second salt must be capable of bonding with the anionic component ofthe first salt to form the solid product material in the aqueous mixtureat a temperature of from 15° C. to 150° C. and under anaerobicconditions.

The second salt also contains an anionic component associated with thecationic component of the second salt to form the second salt. Theanionic component of the second salt may be selected from a wide rangeof counterions to the cationic component of the second salt so long asthe combined cationic component and the anionic component of the secondsalt form a salt that is dispersible, and preferably soluble, in theaqueous mixture in which the first salt and the second salt are mixed,and so long as the anionic component of the second salt does not preventthe combination of the anionic component of the first salt with thecationic component of the second salt in the aqueous mixture to form thesolid product material. Preferably, the anionic component of the secondsalt balances the charge of the cationic component of the second salt inthe second salt. The anionic component of the second salt may beselected from the group consisting of sulfate, chloride, bromide,iodide, acetate, acetylacetonate, phosphate, nitrate, perchlorate,oxalate, citrate, and tartrate.

Certain compounds are preferred for use as the second salt to producethe tetrathiometallate or tetraselenometallate material of the presentinvention. In particular, the second salt is preferably selected fromthe group consisting of FeSO₄, Fe(NO₃)₂, Fe(NO₃)₃, FeCl₂, FeCl₃, ironacetate, iron acetylacetonate, FeBr₂, Fe(ClO₄)₂, Fe(ClO₄)₃, ferriccitrate, NiSO₄, nickel acetate, nickel acetylacetonate, NiCl₂, Ni(NO₃)₂,Ni(ClO₄)₂, Ni(ClO₃)₂, CoSO₄, CoCl₂, cobalt acetate, cobaltacetylacetonate, Co(NO₃)₂, Co(ClO₄)₂, CoI₂, CoBr₂, Co(ClO₃)₂, ZnCl₂,ZnSO₄, zinc acetate, zinc acetylacetonate, ZnBr₂, ZnI₂, Zn(NO₃)₂,Zn(ClO₃)₂, Zn(ClO₄)₂, silver acetate, silver acetylacetonate, AgClO₃,AgClO₄, AgNO₃, SnSO₄, SnCl₂, tin acetate, tin acetylacetonate, SnBr₂,Bi₂(SO₄)₃, BiCl₃, bismuth acetate, bismuth acetylacetonate, and hydratesand mixtures thereof. These materials are generally commerciallyavailable, or may be prepared from commercially available materialsaccording to well-known methods.

The second salt may be contained in an aqueous solution (the secondaqueous solution, as noted above), where, in the process of the presentinvention, the second aqueous solution containing the second salt may bemixed with the first salt or a first aqueous solution containing thefirst salt in the aqueous mixture to form the solid product material.The second salt is preferably dispersible, and most preferably soluble,in the second aqueous solution and is dispersible, and preferablysoluble, in the aqueous mixture containing the first and second salts.The second aqueous solution contains more than 50 vol. % water, or atleast 75 vol. % water, or at least 90 vol. % water, or at least 95 vol.% water, and may contain more than 0 vol. % but less than 50 vol. %, orat most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of anorganic solvent containing from 1 to 5 carbons and selected from thegroup consisting of an alcohol, a diol, an aldehyde, a ketone, an amine,an amide, a furan, an ether, acetonitrile, and mixtures thereof. Theorganic solvent present in the second aqueous solution, if any, shouldbe selected so that the organic compounds in the organic solvent do notinhibit reaction of the anionic component of the first salt with thecationic component of the second salt upon forming an aqueous mixturecontaining the second aqueous solution, e.g., by forming ligands or byreacting with the first or second salts or their respective cationic oranionic components. Preferably, the second aqueous solution contains noorganic solvent. Most preferably the second aqueous solution consistsessentially of water, preferably deionized, and the second salt,although in a less preferred embodiment the second aqueous solution maycontain compounds other than the second salt, such as a buffer.

If the second salt is contained in a second aqueous solution, theconcentration of the second salt in the second aqueous solution may beselected to promote formation of a solid product material having aparticle size distribution with a small mean and/or median particlesize, where the particles have a relatively large surface area, uponmixing the first salt and the second salt in the aqueous mixture. Asnoted above, it has been found that decreasing the instantaneousconcentration of the first salt and/or the second salt during mixing inthe aqueous mixture produces a solid product material comprised ofsmaller particles relative to solid product materials produced from anaqueous mixture containing higher instantaneous concentrations of thefirst and second salts. In an embodiment of the process of theinvention, the second aqueous solution may contain at most 3 moles perliter, or at most 2 moles per liter, or at most 1 mole per liter, or atmost 0.6 moles per liter, or at most 0.2 moles per liter of the secondsalt.

In the process of the present invention, the first salt and the secondsalt are mixed in an aqueous mixture to form the solid product material.The amount of the first salt relative to the amount of the second saltprovided to the aqueous mixture may be selected so that the atomic ratioof the second metal of the second salt to the first metal of the anioniccomponent of the first salt, either molybdenum, tungsten, or vanandium,is from 2:3 to 20:1, or from 1:1 to 10:1. The amount of the first saltand the second salt provided to the aqueous mixture may be selected sothat the atomic ratio of the second metal of the second salt to thefirst metal of the anionic component of the first salt is at least1.5:1, or at least 1.6:1, or at least 2:1, or more than 2:1 sinceselection of a ratio of less than 1.5:1 may lead to incorporation of asmall quantity of the cationic component of the first salt in the solidmaterial product.

In one embodiment, an aqueous mixture of the first salt and the secondsalt may be formed by adding a solid form of the second salt to anaqueous solution containing the first salt (the first aqueous solution).Alternatively, the aqueous mixture of the first salt and the second saltmay be formed by adding a solid form of the first salt to an aqueoussolution containing the second salt (the second aqueous solution). In afurther embodiment, the aqueous mixture of the first and second saltsmay be formed by combining a first aqueous solution containing the firstsalt and a second aqueous solution containing the second salt. Ifdesired, water—preferably deionized—may be added to the aqueous mixtureformed by any of these methods to dilute the aqueous mixture and reducethe concentrations of the first and second salts in the aqueous mixture.

In another embodiment of the process of the present invention, theaqueous mixture of the first and second salts may be formed by addingthe first salt and the second salt into an aqueous solution separatefrom both a first aqueous solution containing the first salt and asecond aqueous solution containing the second salt. The separate aqueoussolution will be referred hereafter as the “third aqueous solution”. Thethird aqueous solution, if utilized, contains more than 50 vol. % water,or at least 75 vol. % water, or at least 90 vol. % water, or at least 95vol. % water, and may contain more than 0 vol. % but less than 50 vol.%, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of anorganic solvent containing from 1 to 5 carbons and selected from thegroup consisting of an alcohol, a diol, an aldehyde, a ketone, an amine,an amide, a furan, an ether, acetonitrile, and mixtures thereof. Theorganic solvent present in the third aqueous solution, if any, should beselected so that the organic compounds in the organic solvent do notinhibit reaction of the anionic component of the first salt with thecationic component of the second salt upon forming the aqueous mixture,e.g., by forming ligands or reacting with the anionic component of thefirst salt or with the cationic component of the second salt.Preferably, the third aqueous solution contains no organic solvent, andmost preferably comprises deionized water.

In an embodiment of the process of the present invention, the first saltand the second salt may be added as solids to the third aqueoussolution. Alternatively, either the first salt in a first aqueoussolution or the second salt in a second aqueous solution may be added tothe third aqueous solution while adding the other salt in solid form toform the aqueous mixture. If desired, water may be added to the aqueousmixture formed by any of these methods to dilute the aqueous mixture andreduce the concentrations of the first and second salts in the aqueousmixture.

In a preferred embodiment of the process of the present invention, theaqueous mixture of the first and second salts may be formed by combininga first aqueous solution containing the first salt and a second aqueoussolution containing the second salt in a third aqueous solution. Thevolume ratio of the third aqueous solution to the first aqueous solutioncontaining the first salt may be from 0.5:1 to 50:1 where the firstaqueous solution preferably contains at most 0.8, or at most 0.4, or atmost 0.2, or at most 0.1 moles of the first salt per liter of the firstaqueous solution. Likewise, the volume ratio of the third aqueoussolution to the second aqueous solution containing the second salt maybe from 0.5:1 to 50:1 where the second aqueous solution preferablycontains at most 3, or at most 2, or at most 1, or at most 0.8, or atmost 0.5, or at most 0.3 moles of the second salt per liter of thesecond aqueous solution.

The first salt and the second salt may be combined in the aqueousmixture, regardless of which method is selected to combine the first andsecond salts, so that the aqueous mixture containing the first andsecond salts contains at most 1.5, or at most 1.2, or at most 1, or atmost 0.8, or at most 0.6 moles of the combined first and second saltsper liter of the aqueous mixture. It has been found that particle sizeof the solid material product produced by mixing the first and secondsalts in the aqueous mixture increases and the surface area of theparticles decreases with increasing concentrations of the salts.Therefore, to limit the particle sizes in the particle size distributionof the solid material product and to increase the relative surface areaof the particles, the aqueous mixture may contain at most 0.8 moles ofthe combined first and second salts per liter of the aqueous mixture,more preferably at most 0.6 moles, or at most 0.4 moles, or at most 0.2moles of the combined first and second salts per liter of the aqueousmixture. The amount of first salt and the total volume of the aqueousmixture may be selected to provide at most 0.4, or at most 0.2, or atmost 0.1, or at most 0.01 moles of the anionic component per liter ofthe aqueous mixture, and the amount of the second salt and the totalvolume of the aqueous mixture may be selected to provide at most 1, orat most 0.8, or at most 0.4 moles of the cationic component per liter ofthe aqueous mixture.

The rate of addition of the first salt and/or the second salt to theaqueous mixture may be controlled to limit the instantaneousconcentration of the first salt and/or the second salt in the aqueousmixture to produce a solid product material comprised of relativelysmall particles having relatively large surface area. Limiting theinstantaneous concentration of one or both salts in the aqueous mixturemay reduce the mean and/or median particle size of the resulting solidproduct material by limiting the simultaneous availability of largequantities of the anionic components of the first salt and largequantities of the cationic components of the second salt that mayinteract to form a solid product material comprised primarily ofrelatively large particles. In an embodiment of the process of thepresent invention, the rate of addition of the first salt and/or thesecond salt to the aqueous mixture is controlled to limit theinstantaneous concentration of the first salt and/or the second salt inthe aqueous mixture to at most 0.05 moles per liter, or at most 0.01moles per liter, or at most 0.001 moles per liter.

The rate of addition of the first salt and/or the second salt to theaqueous mixture may be controlled by limiting the rate of addition of afirst aqueous solution containing the first salt and/or the rate ofaddition of a second aqueous solution containing the second salt to theaqueous mixture. In one embodiment of the process of the presentinvention, the first aqueous solution containing the first salt may beadded to the second aqueous solution containing the second salt, or thesecond aqueous solution may be added to the first aqueous solution,where the solution being added is added in a dropwise manner to theother solution. The rate of addition of drops of the first aqueoussolution to the second aqueous solution or of drops of the secondaqueous solution to the first aqueous solution may be controlled toprovide the desired instantaneous concentration of the first salt or ofthe second salt in the aqueous mixture. In another embodiment, the firstaqueous solution containing the first salt may be dispersed directlyinto the second aqueous solution containing the second salt at acontrolled flow rate to provide a desired instantaneous concentration ofthe first salt in the aqueous mixture. Alternatively, the second aqueoussolution containing the second salt may be dispersed directly into thefirst aqueous solution containing the first salt at a controlled flowrate selected to provide a desired instantaneous concentration of thesecond salt in the aqueous mixture. The first aqueous solution may bedirectly dispersed into the second aqueous solution or the secondaqueous solution may be directly dispersed into the first aqueoussolution at a selected controlled flow rate using conventional means fordispersing one solution into another solution at a controlled flow rate.For example, one solution may dispersed through a nozzle located in theother solution, where the flow of the solution through the nozzle may bemetered by a flow rate control device.

In a preferred embodiment, the first aqueous solution containing thefirst salt and the second aqueous solution containing the second saltare added to a third aqueous solution, preferably simultaneously, at acontrolled rate selected to provide a desired instantaneousconcentration of the first salt and the second salt in the aqueousmixture. The first aqueous solution containing the first salt and thesecond aqueous solution containing the second salt may be added to thethird aqueous solution at a controlled rate by adding the first aqueoussolution and the second aqueous solution to the third aqueous solutionin a dropwise manner. The rate that drops of the first aqueous solutionand the second aqueous solution are added to the third aqueous solutionmay be controlled to limit the instantaneous concentration of the firstsalt and the second salt in the aqueous mixture as desired. In apreferred embodiment, the first aqueous solution containing the firstsalt and the second aqueous solution containing the second salt aredispersed directly into the third aqueous solution at a flow rateselected to provide a desired instantaneous concentration of the firstsalt and the second salt. The first aqueous solution and the secondaqueous solution may be dispersed directly into the third aqueoussolution using conventional means for dispersing one solution intoanother solution at a controlled flow rate. For example, the firstaqueous solution and the second aqueous solution may be dispersed intothe third aqueous solution by pumping the respective solutions throughseparate nozzles located within the third aqueous solution, where theflow of the first and second solutions through the nozzles is metered byseparate flow metering devices.

The particle size distribution of the solid material produced by mixingthe first salt and the second salt in the aqueous mixture is preferablycontrolled by the rate of addition of the first salt and/or the secondsalt to the aqueous mixture, as described above, so that the medianand/or mean particle size of the particle size distribution falls withina range of from 50 nm to 50 μm. In a preferred embodiment, the particlesize distribution of the solid material is controlled by the rate ofaddition of the first and/or second salts to the aqueous mixture so thatthe median and/or mean particle size of the particle size distributionof the solid material may range from at least 50 nm up to 5 μm, or up to1 μm, or up to 750 nm.

The surface area of the solid material particles produced by mixing thefirst salt and the second salt in the aqueous mixture is also preferablycontrolled by the rate of addition of the first salt and/or the secondsalt to the aqueous mixture, as described above, so that the BET surfacearea of the solid material particles is from 50 m²/g to 500 m²/g. In anembodiment, the surface area of the solid material particles iscontrolled by the rate of addition of the first salt and/or the secondsalt to the aqueous mixture so that the BET surface area of the solidmaterial particles is from 100 m²/g to 350 m²/g

The aqueous mixture contains more than 50 vol. % water, or at least 75vol. % water, or at least 90 vol. % water, or at least 95 vol. % water,and may contain more than 0 vol. % but less than 50 vol. %, or at most25 vol. %, or at most 10 vol. %, or at most 5 vol. % of an organicsolvent containing from 1 to 5 carbons and selected from the groupconsisting of an alcohol, a diol, an aldehyde, a ketone, an amine, anamide, a furan, an ether, acetonitrile, and mixtures thereof. Theorganic solvent present in the aqueous mixture, if any, should notinhibit reaction of the anionic component of the first salt with thecationic component of the second salt. Preferably, the aqueous mixturecontains no organic solvent.

The aqueous mixture containing the first salt and the second salt ismixed to facilitate interaction and reaction of the anionic component ofthe first salt with the cationic component of the second salt to formthe solid product material. The aqueous mixture may be mixed by anyconventional means for agitating a solution, for example by mechanicalstirring.

During mixing, the temperature of the aqueous mixture is maintained inthe range of from 15° C. to 150° C., or from 60° C. to 125° C., or mostpreferably from 65° C. to 100° C. In a preferred embodiment of theprocess of the present invention, the temperature of the aqueous mixtureduring mixing is maintained at less than 100° C. so that the mixing maybe conducted without the application of positive pressure necessary toinhibit the water in the aqueous mixture from becoming steam.

Maintaining the temperature of the aqueous mixture in a range of from50° C. to 150° C. may result in production of a solid material having arelatively large surface area and a substantially reduced median or meanparticle size relative to a solid material produced in the same mannerat a lower temperature. It is believed that maintaining the temperaturein the range of 50° C. to 150° C. drives the reaction of the cationiccomponent of the second salt with the anionic component of the firstsalt, reducing the reaction time and limiting the time available for theresulting product to agglomerate prior to precipitation. Maintaining thetemperature in a range of from 50° C. to 150° C. during the mixing ofthe first and second salts in the aqueous mixture may result inproduction of a solid material having a particle size distribution witha median or mean particle size of from 50 nm up to 5 μm, or up to 1 μm,or up to 750 nm; and having a BET surface area of from 50 m²/g up to 500m²/g or from 100 m²/g to 350 m²/g.

The aqueous mixture may be heated using any conventional means forheating a solution being mixed. For example, the aqueous mixture may bemixed in a jacketed mixing apparatus, where heat may be applied to theaqueous mixture by passing steam through the jacket of the mixingapparatus. If utilized, the first aqueous solution, second aqueoussolution, and/or the third aqueous solution may be heated to atemperature within the desired range prior to forming the aqueousmixture by mixing the first and second salts.

The first and second salts in the aqueous mixture may be mixed under apressure of from 0.101 MPa to 10 MPa (1.01 bar to 100 bar). Preferably,the first and second salts in the aqueous mixture are mixed atatmospheric pressure, however, if the mixing is effected at atemperature greater than 100° C. the mixing may be conducted underpositive pressure to inhibit the formation of steam.

During mixing, the aqueous mixture is maintained under anaerobicconditions. Maintaining the aqueous mixture under anaerobic conditionsduring mixing inhibits the oxidation of the solid product material orthe anionic component of the first salt so that the solid materialproduct produced by the process contains little, if any oxygen. It isbelieved that exclusion of oxygen from the solid material increases thecrystallinity of the solid material—if the aqueous mixture is mixed inthe presence of significant quantities of oxygen the resulting productis an amorphous mass that is not useful as a catalyst for upgrading aheavy crude oil. The aqueous mixture may be maintained under anaerobicconditions during mixing by conducting the mixing in an atmospherecontaining little or no oxygen, preferably an inert atmosphere. Themixing of the first and second salts in the aqueous mixture may beconducted under nitrogen, argon, and/or steam to maintain anaerobicconditions during the mixing. In a preferred embodiment of the processof the present invention, an inert gas, preferably nitrogen or steam, iscontinuously injected into the aqueous mixture during mixing to maintainanaerobic conditions and to facilitate mixing of the first and secondsalts in the aqueous mixture.

The first and second salts are mixed in the aqueous mixture at atemperature of from 15° C. to 150° C. under anaerobic conditions for aperiod of time sufficient to permit the formation of solid materialproduct comprised of a plurality of anionic components from the firstsalt and a plurality of cationic components from the second salt. Thefirst and second salt may be mixed in the aqueous mixture for a periodof at least 1 hour, or at least 2 hours, or at least 3 hours, or atleast 4 hours, or from 1 hour to 10 hours, or from 2 hours to 9 hours,or from 3 hours to 8 hours, or from 4 hours to 7 hours to permit theformation of the solid material product. In an embodiment of the processof the invention, the first and/or second salt(s) may be added to theaqueous mixture over a period of from 30 minutes to 4 hours while mixingthe aqueous mixture, and after the entirety of the first and secondsalts have been mixed into the aqueous mixture, the aqueous mixture maybe mixed for at least an additional 1 hour, or 2 hours, or 3 hours or 4hours, or 5 hours to permit the formation of the solid material product.

After completing mixing of the aqueous mixture of the first and secondsalts, a solid material is separated from the aqueous mixture. The solidmay be separated from the aqueous mixture by any conventional means forseparating a solid phase material from a liquid phase material. Forexample, the solid may be separated by allowing the solid to settle fromthe resulting mixture, preferably for a period of from 1 hour to 16hours, and separating the solid from the mixture by vacuum orgravitational filtration or by centrifugation. To enhance recovery ofthe solid, water may be added to the aqueous mixture prior to allowingthe solid to settle. In an embodiment, water may be added to the aqueousmixture in a volume relative to the volume of the aqueous mixture offrom 0.1:1 to 0.75:1. Alternatively, but less preferably, the solid maybe separated from the mixture by centrifugation without first allowingthe solid to settle and/or without the addition of water. The solidmaterial may also be separated from the aqueous mixture by spray dryingthe aqueous mixture.

The separated solid material product may be washed subsequent toseparating the solid material from the aqueous mixture, if desired. Theseparated solid material may be contaminated with minor amounts,typically less than 0.5 wt. %, of the cationic component from the firstsalt and/or the anionic component from the second salt. These minorcontaminants may be removed from the separated solid material by washingthe separated solid material with water. Substantial volumes of watermay be used to wash the separated solid material since the separatedsolid material is insoluble in water, and the yield of solid materialproduct will not be significantly affected by the wash.

The optionally washed separated solid material product may be dried, ifdesired. The separated solid material product may be dried by heatingthe solid material and/or by holding the solid material under vacuum.The solid material may be dried by heating to a temperature of from 35°C. to 75° C. under anaerobic conditions for a period of time sufficientto dry the solid material, typically from 12 hours to 5 days. The solidmaterial may be dried by vacuum by holding the solid material under avacuum for a period of from 12 hours to 5 days. Preferably the solidmaterial is dried by heating to a temperature of from 35° C. to 75° C.under vacuum for a period of 2 to 4 days.

The solid material may be produced from the first and second salts inrelatively good yield. The solid material may be produced at a molaryield of at least 45% up to 95%, or up to 90%, or up to 85% from thefirst and second salts.

The solid material separated from the aqueous mixture, optionally washedand/or optionally dried, is comprised of a) the first metal of theanionic component of the first salt; and b) the second metal of thecationic component of the second salt, wherein at least a portion of thesolid material separated from the aqueous mixture has a structureaccording to a formula selected from the group consisting of formula(I), formula (II), formula (III), and formula (IV);

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, and Q iseither sulfur or selenium;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃.

The solid material separated from the aqueous mixture may be comprisedof a plurality of anionic components of the first salt and a pluralityof cationic components from the second salt in which anionic componentsfrom the first salt in the solid material are bonded with at least aportion of the cationic components from the second salt in the solidmaterial in two or more repeating units. The solid material may becomprised of alternating atoms of the first metal of the anioniccomponent of the first salt and the second metal of the cationiccomponent of the second salt bonded to and linked by two sulfur atoms.The solid material may comprise alternating M¹S₄ and M²S₄ tetrahedralformations, where each tetrahedral formation shares at least two sulfuratoms with an adjacent tetrahedral formation, where M¹ is the firstmetal of the anionic component of the first salt and M² is the secondmetal of the cationic component of the second salt. The solid materialmay be comprised of alternating atoms of the first metal of the anioniccomponent of the first salt and the second metal of the cationiccomponent of the second salt bonded to an linked to and linked by twoselenium atoms. The solid material may comprise alternating M¹Se₄ andM²Se₄ tetrahedral formations, where each tetrahedral formation shares atleast two selenium atoms with an adjacent tetrahedral formation, whereM¹ is the first metal of the anionic component of the first salt and M²is the second metal of the cationic component of the second salt.

In an embodiment of the present invention, the solid material separatedfrom the aqueous mixture is comprised of the first metal of the anioniccomponent of the first salt and the second metal of the cationiccomponent of the second salt, where the solid material is comprised ofat least three linked chain elements, the chain elements being comprisedof a first chain element including the first metal of the anioniccomponent of the first salt and having a structure according to formula(V) and a second chain element including the second metal of thecationic component of the second salt and having a structure accordingto formula (VI)

where M¹ is molybdenum, tungsten, or vanadium; M² is selected from thegroup consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La,Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, and Sn; and where Q is either sulfuror selenium. In this embodiment, the solid material contains at leastone first chain element and at least one second chain element. At leasta portion of the chain elements in the solid material are linked bybonds between the two sulfur atoms or the two selenium atoms of a chainelement and the metal of an adjacent chain element.

In an embodiment of the present invention, the solid material separatedfrom the aqueous mixture is comprised of monomeric units that repeat inthe solid material to form a polymer, where a monomeric unit iscomprised of a first metal of the anionic component of the first saltand a second metal of the cationic component from the second salt,bridged by, and bonded to, two sulfur atoms or two selenium atoms. Thesolid material may be comprised of units having the structure shown informula VII:

where M¹ is molybdenum, tungsten, or vanadium; M² is selected from thegroup consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La,Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, and Sn; Q is either sulfur orselenium; and x is at least 2, or at least 5, or at least 10.

Furthermore, the solid material may have a two-dimensional or athree-dimensional polymeric structure with alternating metal centers ofthe second metal of the cationic component from the second salt and themolybdenum, tungsten, or vanadium of the anionic component from thefirst salt bridged by two sulfur atoms or bridged by two selenium atoms.The two- and/or three-dimensional polymeric structure of a solidmaterial produced hereby may have “holes” in its structure, in which asecond metal of the cationic component from the second salt is missingas an alternating metal center. The two- and/or three-dimensionalpolymeric structure may contain a portion of the second metal of thecationic component of the second salt within interstices in thepolymeric structure or in holes in the polymeric structure, where theportion of the second metal of the cationic component of the second saltlocated in the interstices or holes in the polymeric structure is notbonded with an anionic component from the first salt that forms a partof the polymeric structure and/or is not bonded with a sulfur atom or aselenium atom included in the polymeric structure.

The solid material separated from the aqueous mixture is typically atleast partially crystalline, where the cystallinity of the solidmaterial may be determined by x-ray powder diffraction. The solidmaterial may be from 15% to 100% crystalline, or from 25% to 99%crystalline, of from 35% to 95% crystalline, or at least 20%crystalline, or at least 30% crystalline, or at least 40% crystalline,or at least 50% crystalline, or at least 60% crystalline, or at least70% crystalline, or at least 75% crystalline. The solid materialtypically has a tetrahedral crystalline structure. The solid materialalso typically comprises alternating M^(I)S₄ and M^(II)S₄ tetrahedralformations or alternating M¹Se₄ and M²Se₄ tetrahedral formations, whereeach tetrahedral formation shares two sulfur atoms or two selenium atomswith an adjacent tetrahedral formation, and where M^(I) is the metal ofthe anionic component of the first salt and M^(II) is the metal of thecationic component of the second salt.

The solid material separated from the aqueous mixture typicallycomprises at most 0.1 wt. %, or at most 0.05 wt. %, or at most 0.01 wt.% oxygen. The oxygen content of the solid material may be determined byneutron activation, for example, in accordance with ASTM Method E385. Ina preferred embodiment, oxygen is not detectable in the solid material.Oxygen is undesirable in the solid material when the solid material isto be used as a catalyst for hydrocracking a disadvantaged crude oil.The catalytic activity of the solid material as a hydrocracking catalystis, in part, believed to be due to the availability of electrons fromthe solid material catalyst to stabilize cracked molecules in the crudeoil. Due to its electronegativity, oxygen tends to reduce theavailability of electrons from the solid material when it is present inthe solid material in appreciable quantities. Also, as noted above, itis believed that inclusion of any significant quantity of oxygen in thesolid material renders the solid material amorphous and not crystalline,which may substantially decrease the surface area of the solid materialand reduce the effectiveness of the solid material as a catalyst.

The solid material separated from the aqueous mixture may contain atmost 0.5 wt. %, or at most 0.1 wt. %, or at most 0.01 wt. % of thecationic component of the first salt. The cationic content of the firstsalt included in the solid material may be measured by x-rayfluorescence. The cationic component of the first salt may be anundesirable contaminant in the solid material. In an embodiment of theprocess of the present invention, the cationic component of the secondsalt is utilized in an atomic ratio to the metal of the anioniccomponent of the first salt of greater than 1.5:1, or at least 1.6:1, orat least 2:1, or greater than 2:1 to ensure that the solid materialcontains less than 0.5 wt. % of the cationic component of the firstsalt. It is believed that the cationic component of the first salt maybecome included in the solid material if insufficient cationic componentof the second salt is present to counterbalance the charge of theanionic component of the first salt upon formation of the solidmaterial, therefore, sufficient cationic component of the second saltmay be provided to reduce or eliminate the presence of the cationiccomponent of the first salt in the solid material product.

The solid material separated from the aqueous mixture may contain lessthan 0.5 wt. % of ligands other than sulfur-containing ligands orselenium-containing ligands. Ligands, other than ligands formed from thesulfur or selenium provided by the first are not desirable in the solidmaterial product since they may end-cap the compound formed by thecombined cationic component of the second salt and the anionic componentof the first salt, inhibiting addition of further repeating units of thecationic component of the second salt and the anionic component of thefirst salt to the end-capped compound. To inhibit the incorporation ofsuch ligands into the solid material, the first salt and second saltsare selected so that the cationic component of the first salt and theanionic component of the second salt are not capable of forming ligandswith the cationic component of the second salt or the anionic componentof the first salt or the solid material formed by repeating unitsthereof or with any component of the aqueous mixture.

The solid material separated from the aqueous mixture has a particlesize distribution. The particle size distribution may have a medianparticle size and/or a mean particle size of from 50 nm to 50 μm, orfrom 75 nm to 10 μm, or from 100 nm to 1 μm, most preferably from 50 nmto 1 μm. In an embodiment of the invention, the solid material may havea particle size distribution with a mean and/or median particle size offrom 50 nm up to 5 μm, or up to 1 μm, or up to 750 nm.

It is preferable that the solid material have a particle sizedistribution with a mean and/or median particle size of at least 50 nmso that the solid material may be utilized to hydrocrack and/orhydrotreat a heavy crude oil and be easily separated from thehydrocarbon feedstock, hydrocarbon product, and/or a byproduct stream.If the solid material has a mean and/or median particle size less than50 nm, the solid material may be soluble in the hydrocarbon feedstock,product, and/or byproduct stream, rendering the solid material catalystdifficult to separate from hydrocarbon feedstock, product, and/orbyproduct stream.

It is further preferable that the solid material have a particle sizedistribution having a mean and/or median particle size of at most 5 μm,more preferably of at most 1 μm, so that the solid material will have arelatively large surface area. A relatively large surface area isdesirable when the solid material is used as a catalyst in hydrocrackingand/or hydrotreating a hydrocarbon feedstock to provide high catalyticactivity. The solid material particles may have a mean BET surface areaof from 50 m²/g to 500 m²/g, or from 100 m²/g to 350 m²/g.

To facilitate a better understanding of the present invention, thefollowing examples of certain aspects of some embodiments are given. Inno way should the following examples be read to limit, or define, thescope of the invention.

Example 1

A cobalt tetrathiomolybdate material, at least a portion of which had astructure according to formula (VIII), was produced by a process inaccordance with the process of the present invention.

65.08 grams of (NH₄)₂MoS₄ were dissolved in 0.5 liters of deionizedwater under nitrogen and heated to 60° C. with stirring. A 240 millitersolution of 62.01 grams of Na₂CO₃.H₂O in deionized water was addeddropwise to the heated stirred (NH₄)₂MoS₄ solution over 2 hours. Theresulting solution was then stirred for 3 hours at 80° C. and thenallowed to cool to ambient to produce a Na₂MoS₄ solution. Separately,572.9 grams of CoSO₄ was dissolved in 1 liter of deionized water. 2liters of water were heated to 80° C. under N₂, and the Na₂MoS₄ solutionand the CoSO₄ solution were separately charged to the heated water underN₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitateformed immediately, and the resulting slurry was stirred at 90° C. for 2hours, then allowed to cool to 45° C. A solid material was separatedfrom the slurry by continuous centrifuge at 12,000 gauss. The solidmaterial was collected and washed until the liquid wash effluent had aneutral pH and a conductivity of 0.19 μS at 32.0° C. The washed solidswere then dried under vacuum at 60° C. 75.5 grams of solid product wererecovered.

Semi-Quantitative XRF of the recovered solid product measured, on a massbasis: 23.266% S; 31.917% Fe; and 18.826% Mo. The BET surface area ofthe solid material was measured to be 7.52 m²/gram and the solidmaterial's single-point adsorption total pore volume was measured to be0.017 cm³/gram. The solid material product had an adsorption averagepore width of 89.6 Å.

Example 2

An iron tetrathiomolybdate material, at least a portion of which had astructure according to formula (IX), was produced from ferrous iron by aprocess in accordance with the process of the present invention.

49.6 grams of Na₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed undernitrogen in 1.5 liters of deionized water at 80° C. to form a Na₂MoS₄solution. Separately, 194.6 grams of FeSO₄.7H₂O was mixed in 1 liter ofdeionized water. Approximately 200 mg of sodium dithionite was added tothe iron solution to remove any oxygen. 2 liters of deionized water wereheated separately to a temperature of 80° C., and the Na₂MoS₄ solutionand the FeSO₄ solution were separately charged to the heated water underN₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitateformed immediately, and the resulting slurry was stirred at 80° C. for2.5 hours under nitrogen, then allowed to cool. A solid material wasseparated from the slurry by continuous centrifuge at 12,000 gauss. Thesolid material was collected and washed until the liquid wash effluenthad a neutral pH and a conductivity of 0.36 μS at 26.0° C. The washedsolids were then dried under vacuum at 55° C. 66.12 grams of solidproduct were recovered.

Semi-Quantitative XRF of the solid product measured, on a mass basis:23.266% S; 31.917% Fe; and 18.826% Mo. The BET surface area of the solidproduct was measured to be 7.52 m²/gram and the solid product'ssingle-point adsorption total pore volume was measured to be 0.017cm³/gram. The solid product had an adsorption average pore width of 89.6Å.

Example 3

A nickel tetrathiomolybdate material, at least a portion of which had astructure according to formula (X), was produced by a process inaccordance with the process of the present invention.

49.6 grams of Na₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed undernitrogen in 1.5 liters of deionized water at 80° C. to form a Na₂MoS₄solution. Separately, 489.1 grams of NiSO₄ were mixed in 1 liter ofdeionized water and heated to 80° C. 1 liter of deionized water wereheated separately to a temperature of 71° C., and the Na₂MoS₄ solutionand the NiSO₄ solution were separately charged to the heated water underN₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitateformed immediately, and the resulting slurry was stirred at 80° C. for2.5 hours under nitrogen, then allowed to cool. A solid material wasseparated from the slurry by continuous centrifuge at 8000 gauss. Thesolid material was collected and washed until the liquid wash effluenthad a neutral pH and a conductivity of 50 μS at 24.3° C. The washedsolids were then dried under vacuum at 55° C. 50.05 grams of solidproduct were recovered.

Example 4

A zinc tetrathiomolybdate material was produced by a process inaccordance with the process of the present invention. 42.4 grams ofNa₂CO₃.H₂O and 52.07 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 4liters of deionized water at 75° C. to form a Na₂MoS₄ solution.Separately, 114.9 grams of ZnSO₄.H₂O were mixed in 4 liters of deionizedwater and heated to 75° C. 7 liters of deionized water were heatedseparately to a temperature of 87° C., and the Na₂MoS₄ solution and theZnSO₄.H₂O solution were separately charged to the heated water under N₂via pneumatic pump through 2″×0.02″ nozzles. A yellow ochre precipitateformed immediately, and the resulting slurry was stirred at 80° C. for2.5 hours under nitrogen, then allowed to cool. A solid material wasseparated from the slurry by continuous centrifuge at 8000 gauss. Thesolid material was collected and washed until the liquid wash effluenthad a pH of 4-5 and a conductivity of 55 μS at 26.1° C. The washedsolids were then dried under vacuum at 55° C. 41.72 grams of solidproduct were recovered. Semi-Quantitative XRF of the solid productmeasured, on a mass basis: 7.953% Na; 21.311% S; 44.636% Zn; 14.458% Mo;and less than 0.005% Al, Si, Cl, Fe and Ni. The solid product wasparticulate and was found to have a multimodal particle sizedistribution between 0.05 μm to 878 μm with the highest particle volumedistribution centered at 150 μm as determined by laser diffractometryusing a Mastersizer S made my Malvern Instruments. The BET surface areaof the solid product was measured to be 32.5 m²/gram and the solidproduct's single-point adsorption total pore volume was measured to be0.061 cm³/gram. The solid product had a pore size distribution, wherethe median pore size diameter was determined to be 74.9 Angstroms.

Example 5

A tin tetrathiomolybdate material was produced by a process inaccordance with the process of the present invention. 42.4 grams ofNa₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 4liters of deionized water at 80° C. to form a Na₂MoS₄ solution.Separately, 150.3 grams of tin (II) sulfate were mixed in 2.5 liters ofdeionized water and heated to 80° C. 3 liters of deionized water wereheated separately to a temperature of 80° C., and the Na₂MoS₄ solutionand the tin (II) sulfate solution were separately charged to the heatedwater under N₂ via pneumatic pump through 2″×0.02″ nozzles. A yellowochre precipitate formed immediately, and the resulting slurry wasstirred at 80° C. for 3 hours under nitrogen, then allowed to cool. Asolid material was separated from the slurry by continuous centrifuge at8000 gauss. The solid material was collected and washed until the liquidwash effluent had a pH of 5 and a conductivity of 0.71 μS at 22.4° C.The washed solids were then dried under vacuum at 55° C. 147.1 grams ofsolid product were recovered.

Semi-Quantitative XRF of the solid product measured, on a mass basis:12.749% S; 61.775% Sn; 9.516% Mo; 0.998% Zn; and less than 0.049% Mg,Al, Si, Cu, and Pb. The BET surface area of the solid product wasmeasured to be 114.8 m²/gram

The present invention is well adapted to attain the ends and advantagesmentioned as well as those that are inherent therein. The particularembodiments disclosed above are illustrative only, as the presentinvention may be modified and practiced in different but equivalentmanners apparent to those skilled in the art having the benefit of theteachings herein. Furthermore, no limitations are intended to thedetails of construction or design herein shown, other than as describedin the claims below. It is therefore evident that the particularillustrative embodiments disclosed above may be altered or modified andall such variations are considered within the scope and spirit of thepresent invention. While compositions and methods are described in termsof “comprising,” “containing,” or “including” various components orsteps, the compositions and methods can also “consist essentially of” or“consist of” the various components and steps. Whenever a numericalrange with a lower limit and an upper limit is disclosed, any number andany included range falling within the range is specifically disclosed.In particular, every range of values (of the form, “from a to b,” or,equivalently, “from a-b”) disclosed herein is to be understood to setforth every number and range encompassed within the broader range ofvalues. Also, the terms in the claims have their plain, ordinary meaningunless otherwise explicitly and clearly defined by the patentee.Moreover, the indefinite articles “a” or “an”, as used in the claims,are defined herein to mean one or more than one of the element that itintroduces.

1. A method for producing a thiometallate or selenometallate material,comprising: mixing a first salt and a second salt in an aqueous mixtureunder anaerobic conditions, where, during mixing the aqueous mixture hasa temperature of from 15° C. to 150° C., and wherein the first saltcomprises a cationic component containing one or more metals selectedfrom the group consisting of an alkali metal, an alkaline earth metal,and mixtures thereof and comprises an anionic component containing afirst metal selected from the group consisting of Mo, W, and V where theanionic component is selected from the group consisting of MoS₄ ²⁻,MoSe₄ ²⁻, WS₄ ²⁻, WSe₄ ²⁻, VS₄ ³⁻, VSe₄ ³⁻ and mixtures thereof, andwherein the second salt comprises a cationic component comprising asecond metal in any non-zero oxidation state selected from the groupconsisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr,Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, and mixtures thereof, where thefirst and second salts are soluble in the aqueous mixture; separating asolid material from the aqueous mixture comprising a) the first metal ofthe anionic component of the first salt; and b) the second metal of thecationic component of the second salt, wherein at least a portion of thesolid material separated from the aqueous mixture has a structureaccording to a formula selected from the group consisting of formula(I), formula (II), formula (III), and formula (IV);

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, and Q iseither sulfur or selenium;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least oneM is the first metal and at least one M is the second metal, Q is eithersulfur or selenium, and X is selected from the group consisting of SO₄,PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl,Br, I, ClO₄, and NO₃.
 2. The method of claim 1 wherein the amount of thefirst salt and the amount of the second salt mixed in the aqueousmixture are selected to provide an atomic ratio of the second metal tothe first metal of greater than 1.6:1.
 3. The method of claim 1 whereinthe solid material separated from the aqueous mixture comprises at most0.1 wt. % oxygen.
 4. The method of claim 1 wherein the solid materialseparated from the aqueous mixture contains at most 0.5 wt. % of thecationic component of the first salt.
 5. The method of claim 1 whereinthe amount of the first salt and the total volume of the aqueous mixtureare selected to provide at most 0.2 moles of the anionic component fromthe first salt per liter of the total volume of the aqueous mixture, andwhere the amount of the second salt and the total volume of the aqueousmixture are selected to provide at most 1 mole of the cationic componentof the second salt per liter of the total volume of the aqueous mixture.6. The method of claim 1 wherein the first salt is contained in a firstaqueous solution and the second salt is contained in a second aqueoussolution, and the first salt and the second salt are mixed in theaqueous mixture by mixing the first aqueous solution and the secondaqueous solution.
 7. The method of claim 6 wherein the first aqueoussolution containing the first salt and the second aqueous solutioncontaining the second salt are added to a third aqueous solution to formthe aqueous mixture.
 8. The method of claim 7 wherein the volume ratioof the third aqueous solution to the first aqueous solution is from0.5:1 to 50:1 where the first aqueous solution contains at most 0.8moles per liter of the first salt and the volume ratio of the thirdaqueous solution to the second aqueous solution is from 0.5:1 to 50:1where the second aqueous solution contains at most 3 moles per liter ofthe second salt.
 9. The method of claim 7 where the first aqueoussolution and the second aqueous solution are added to the third aqueoussolution and mixed in the third aqueous solution such that theinstantaneous concentration of the first salt in the aqueous mixture isat most 0.05 moles per liter and such that the instantaneousconcentration of the second salt in the aqueous mixture is at most 0.05moles per liter.
 10. The method of claim 6 further comprising the stepof forming the first aqueous solution containing the first salt bymixing a salt comprising an alkali metal carbonate or an alkaline earthmetal carbonate and an aqueous solution containing a salt selected fromthe group consisting of (NH₄)₂MoS₄, (NH₄)₂MoSe₄, (NH₄)₂WS₄, (NH₄)₂WSe₄,(NH₄)₃VS₄, (NH₄)₃VSe₄ and mixtures thereof at a temperature of from 50°C. to 150° C. under anaerobic conditions, where ammonia gas and carbondioxide are evolved and degassed during mixing the salt comprising thealkali metal carbonate or alkaline earth metal carbonante and theaqueous solution containing the salt selected from the group consistingof (NH₄)₂MoS₄, (NH₄)₂MoSe₄, (NH₄)₂WS₄, (NH₄)₂WSe₄, (NH₄)₃VS₄, (NH₄)₃VSe₄and mixtures thereof.
 11. The method of claim 1 wherein the solidmaterial separated from the aqueous mixture is particulate and has aparticle size distribution, where the mean particle size or the medianparticle size of the particle size distribution of the solid material isfrom 50 nm to 10 μm.
 12. The method of claim 1 wherein the solidmaterial separated from the aqueous mixture is particulate where theparticles have an average BET surface area of from 50 m²/g to 500 m²/g.13. The method of claim 1 wherein the solid material is at least 20%crystalline.
 14. The method of claim 1 wherein the aqueous mixturecontains more than 0 vol. % but less than 50 vol. % of an organicsolvent containing from 1 to 5 carbons and selected from the groupconsisting of an alcohol, a diol, an aldehyde, a ketone, an amine, anamide, a furan, an ether, acetonitrile, and mixtures thereof where thefirst salt and the second salt are soluble in the aqueous mixture. 15.The method of claim 1 wherein the solid material comprises alternatingM¹S₄ and M²S₄ tetrahedral formations, where each tetrahedral formationshares two sulfur atoms with an adjacent tetrahedral formation, andwhere M¹ is the first metal and M² is the second metal.
 16. The methodof claim 1 wherein the solid material separated from the aqueous mixtureis comprised of alternating atoms of the first metal and the secondmetal bonded to and linked by two sulfur atoms.
 17. The method of claim1 wherein the solid material separated from the aqueous mixture iscomprised of at least three linked chain elements, the chain elementsbeing comprised of a first chain element including the first metal andhaving a structure according to formula (V) and a second chain elementincluding the second metal and having a structure according to formula(VI)

where M¹ is the first metal, where M² is the second metal, and where Qis either sulfur or selenium; where the solid material contains at leastone first chain element and at least one second chain element, and whereat least a portion of the chain elements in the solid material arelinked by bonds between two sulfur atoms or two selenium atoms of achain element and the metal of an adjacent chain element.
 18. The methodof claim 1 wherein the solid material is comprised of a plurality ofanionic components from the first salt and a plurality of cationiccomponents from the second salt where the anionic components from thefirst salt are bonded with at least a portion of the cationic componentsfrom the second salt in two or more repeating units.
 19. The method ofclaim 1 wherein the solid material separated from the aqueous mixture iscomprised of monomeric units that repeat in the solid material so thatthe solid material product is a polymer formed of the repeatingmonomeric units, where a monomeric unit is comprised of the first metaland the second metal bridged by, and bonded to, two sulfur atoms or twoselenium atoms, the polymer having the structure of formula (VII):

where M¹ is the first metal, M² is the second metal, Q is either sulfuror selenium, and x is at least
 2. 20. The method of claim 1 wherein thesolid material separated from the aqueous mixture contains less than 0.5wt. % of ligands other than sulfur or selenium containing ligands. 21.The method of claim 1 further comprising the step of washing the solidmaterial with water subsequent to separation of the solid material fromthe aqueous mixture.
 22. The method of claim 1 further comprising thestep of drying the separated solid material.